 专业专注POM TR-20日本宝理 15%滑石填料POM
供应POM TR-20日本宝理 加15%滑石填料 高刚性 低翘曲。
| 拉伸强度(引张强度) |
|
ASTM D638/ISO 527 |
59 |
kg/cm²(MPa)[Lb/in2] |
| 断裂伸长率 |
|
ASTM D638/ISO 527 |
|
% |
| 拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm²(MPa)[Lb/in2] |
| 拉伸屈服伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
| 拉伸断裂伸长率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
| 弯曲模量(弯曲弹性率) |
|
ASTM D790/ISO 178 |
4100 |
kg/cm²(MPa)[Lb/in2] |
| 弯曲强度 |
|
ASTM D790/ISO 178 |
96 |
kg/cm²(MPa)[Lb/in2] |
| 洛氏硬度 |
|
ASTM D785 |
|
|
| IZOD 缺口冲击强度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| Charpy冲击强度 |
23℃ （缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| -30℃（缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 23℃（无缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| -30℃（无缺口） |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
| 物性性能 |
比重（密度） |
|
ASTM D792/ISO 1183 |
1.53 |
|
| 成型收缩率 |
|
ASTM D955 |
|
% |
| 熔融指数（流动系数） |
200℃/5kg |
ASTM D1238/ISO 1133 |
|
g/10min |
| 220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
| 吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
|
% |
| 热性能 |
热变形温度 |
退火 |
ASTM D648/ISO 75 |
|
℃（℉） |
| 未退火 |
ASTM D648/ISO 75 |
|
℃（℉） |
| 维卡软化点 |
|
ASTM D1525/ISO R306 |
|
℃（℉） |
| 熔点 |
|
- |
|
℃（℉） |
| 燃烧性（率） |
|
UL94 |
HB |
|
| 线性膨胀系数 |
|
ASTM D696/ISO 11359 |
7 |
mm/mm.℃ |
| 电气性能 |
介电常数 |
100HZ |
ASTM D150/IEC 60250 |
|
|
| 1MHZ |
ASTM D150/IEC 60250 |
|
|
| 体积电阻率 |
|
ASTM D257/IEC 60093 |
2.0 x 10^14 |
Ω.cm |
| 表面电阻率 |
|
ASTM D257/IEC 60093 |
9.0 x 10^15 |
Ω |
| 耐电弧性 |
|
ASTM D495/IEC 60112 |
|
|
| 加工条件 |
干燥条件 |
|
|
|
| 专业专注POM（聚甲醛/赛钢料），主要销售 玻纤/碳纤增强POM，防火POM，抗紫外线POM，耐候级POM，加铁氟龙POM，防静电/导电POM，另有其它牌号塑胶原料供应商，详情请联系工程塑胶供应商李小姐。 |